Fig. 1: Anchoring-assisted intermediate direct pinning for quasi-2D perovskites. a Schematic reaction coordinate of the intermediate direct pinning (IDP) process of quasi-2D perovskites. b, c Grazing-incident x-ray diffraction pattern corresponding 1D XRD profile of pristine (b) and A-IDP (c) perovskite thin films. d X-ray diffraction spectra of n\u2009=\u20091 PEA2PbBr4 perovskites without and with CCA additives as molecular anchor. e Relative content of carbon and nitrogen to lead in perovskite films determined from XPS. f Normalized UV-vis absorption and PLE spectra of pristine and A-IDP perovskite films. g Steady-state PL spectra of perovskite films.<\/p>\n The intermediate phase was first induced by exploiting a strong cation-\u03c0 interaction between PEA+ and ammonium (NH4+) ions that retards crystallization toward low-n phases. Before thermodynamically driven crystallization of low-n phases occurs, these intermediate phases can exist uniformly in a metastable state without the broadening of phases that occurs during one-step precursor-to-crystal conversion. Here, tetrahydrofuran (THF) as a volatile Lewis-base solvent and CCA as an anchoring molecule were applied to the intermediate film to achieve an anchoring-assisted intermediate direct pinning method (A-IDP) (Supplementary Fig.\u00a01<\/a>). The CCA-THF solution was applied to the intermediate film and immediately spin-dried (hereafter referred as exposure duration, DE\u2009=\u20090\u2009s); this process substitutes the CCA ligand for the intermediate complex of PEA, simultaneously removing residual solvents to prohibit diffusion-induced broad phase distribution of quasi-2D crystals. We performed the in-situ UV-Vis absorption analysis during the crystallization to monitor the kinetic changes in phase distribution via the A-IDP process (Supplementary Fig.\u00a02<\/a>). The pristine film without A-IDP process exhibited slowly increasing absorbance corresponding to the n\u2009=\u20091, 2, 3 phases with each different rate, suggesting the intermixing between low-n phases during the crystallization process. In contrast, the A-IDP film maintained the initial relative phase distribution throughout the whole crystallization process; this suggests the A-IDP process can kinetically fix the phase distribution and inhibit intermixing among the low-n phases.<\/p>\n Grazing incidence wide-angle X-ray scattering (GIWAXS) patterns provided the crystal structure and orientation of the perovskite after A-IDP (Fig.\u00a01b, c<\/a>). The pristine perovskite film had highly-ordered diffraction peaks that correspond to the orientation of low-n phases (n\u2009=\u20091\u20133) toward the out-of-plane (Qz) direction; this result suggests the spontaneous aggregation of perovskite crystals into low-n phases during the crystallization process. The 1D XRD pattern showed intense diffraction peaks of low-dimensional phases oriented toward the Qz direction, which is an unfavorable configuration for charge transport toward the direction of charge injection during device operation19<\/a>.<\/p>\n In contrast, perovskite film prepared by A-IDP showed only ring-patterned scattering peaks, which correspond to 3D CsPbBr3 (5.8\u2009\u00c5) oriented mainly toward the Qz direction, indicating increased crystallinity of medium-n phases toward the vertical direction that can benefit on efficient charge transport in LED devices. Importantly, there were no diffraction peaks at low angle <1.0\u2009\u00c5\u22121, indicating the removal of highly-ordered low-n phases. A-IDP significantly reduced the surface root-mean-square (RMS) from 5.160\u2009nm to 0.808\u2009nm (Supplementary Fig.\u00a03<\/a>); this change indicates redistribution of aggregated low-n phases into uniformly distributed nanosized medium-n phases. Increasing DE up to 20\u2009s intensified the diffraction peak of 3D phases in GIWAXS (Supplementary Fig.\u00a04<\/a>). However, complete removal of quasi-2D phases created pinholes at grain boundaries; to avoid this, the selective removal of excess intermediate phases requires precise control over short reaction times (Supplementary Fig.\u00a05<\/a>).<\/p>\n We examined the incorporation of CCA molecule into quasi-2D crystal structure by comparing pure n\u2009=\u20091 PEA2PbBr4 crystals prepared by solvent-IDP (S-IDP) process with only THF solvent, with those prepared via the A-IDP process with CCA-THF solution. The A-IDP process applied to pure n\u2009=\u20091 PEA2PbBr4 crystals led to a reduction in lattice distance from 16.72\u2009\u00c5 to 16.63\u2009\u00c5, due to the smaller molecular size of CCA compared to that of PEA and strong coordination between PbBr64\u2212 octahedra and the \u2013COOH and \u2013C\u2009=\u2009O groups in CCA (Fig.\u00a01d<\/a>). Fourier-transform infrared (FTIR) analysis confirmed the removal of PEA after S-IDP process and incorporation of the CCA molecule after the A-IDP process (Supplementary Fig.\u00a06a\u2013c<\/a>).<\/p>\n To further identify the chemical composite after the A-IDP process, XPS analysis was performed on samples with DE ranging from 0\u2009s (A-IDP) to 20\u2009s (Supplementary Fig.\u00a06d\u2013i<\/a>). The core level peaks of C 1\u2009s and N 1\u2009s originating from PEA cations gradually diminished as DE increased, consistent with the removal of low-n phases observed through GIWAXS. A comparison of the N\/Pb atomic ratio revealed a stoichiometric shift from average value of <n>\u2009=\u20093 (N\/Pb\u2009=\u20091.25) toward <n>\u2009=\u20095 (N\/Pb\u2009=\u20091.0) after DE\u2009=\u20090\u2009s, which eventually became a\u00a03D-like composite with N\/Pb ratio <0.4 as DE increased (Fig.\u00a01e<\/a>). The peak position and relative stoichiometry of Pb 4\u2009f and Br 3\u2009d peak were retained; this observation indicates selective removal of metastable PEA cations without any compositional change in the perovskite crystal.<\/p>\n The influence of phase distribution on the behavior of charge carriers was elucidated through UV-vis absorption and photoluminescence excitation (PLE) spectra (Fig.\u00a01f<\/a>). The pristine film exhibited a distinct excitonic peak feature associated with low-n phases (~425\u2009nm and ~450\u2009nm) situated well above the onset of absorption (~490\u2009nm). In contrast, this feature was markedly subdued in the A-IDP film, indicative of a smoother energy landscape attributed to the restrained formation of energetically discrete low-n phases. Moreover, the pristine film showed a gradual decrease in PLE intensity relative to the absorbance in the higher energy (shorter wavelength) region, while that of the A-IDP film was mostly maintained. This increased disparity between PLE and absorbance in the pristine film implies a considerable loss of excited charge carriers at energies well above the band gap, contributing less to the light emission. Conversely, a relatively larger proportion of charge carriers in the A-IDP film contributes to light emission, suggesting improved funnelling of the excess photoexcited energy to the emitting state. As a result, the A-IDP films exhibited substantially increased PL intensity and PL lifetime compared to that of pristine films (Fig.\u00a01g<\/a> and Supplementary Fig.\u00a07<\/a>).<\/p>\n Phase regulation by cation-\u03c0 intermediate complex<\/p>\n The formation of the intermediate phase was triggered by incorporating highly reactive methylenediamonium dichloride (MDACl2) into the precursor solution. In solution, MDACl2 rapidly degrades into NH4+ and hexamethylenetetramine (HMTA)20<\/a>. Exploiting this proposed reaction scheme, we induced the formation of an intermediate complex with PEA+. First, the steady-state UV-Vis absorption spectra of mixture solution of MDACl2 and PEA+ revealed the emergence of a new absorption band at ~400\u2009nm as a result of formation of a new charge-transfer (CT) complex; considering no observation of CT complex among any of the precursor solutions or even with the pre-existing \u03c0-\u03c0 stacking in PEABr-only solution, strong coordination with charge transfer is present in the MDA-PEA mixture solution with the additional electrostatic interaction with \u03c0 electrons to form CT states21<\/a> (Supplementary Fig.\u00a08a\u2013c<\/a>).<\/p>\n To unveil the origin of the CT complex, we analysed the 1H nuclear magnetic resonance (NMR) spectra at different ratios of PEA+ to MDACl2 to obtain specific information on interactions among chemical species in solution (Supplementary Fig.\u00a08d\u2013i<\/a>). Most peaks exhibited a slight downfield-shift (higher ppm) due to the increase in solution acidity with addition of MDA2+. As the addition ratio of MDACl2 increased, the peak associated with the -NH3+ group of PEA+ shifted gradually downfield from 7.94 ppm to 8.24\u2009ppm in same stoichiometric ratio; this result indicates deshielding of protons induced by the acidified solution. The protons from NH4+ showed a 1:1:1 triplet peak (with splitting due to spin\u2212spin coupling of 1H to the quadrupolar 14N nucleus), which also shifted downfield. In contrast, the C6H5 peak in PEA+ shifted gradually upfield as the MDACl2 ratio increased, despite the increasing acidity of the solution; this result suggests instead that additional shielding of protons occurred by coordination of \u03c0 electrons with Br\u00f8nsted\u2013Lowry acid.<\/p>\n To determine the configuration of PEA+ here, we conducted 2D 1H Nuclear Overhauser Effect Spectroscopy (NOESY), which shows through-space interactions of characteristic protons within 5\u2009\u00c5 (Fig.\u00a02a, b<\/a>)21<\/a>. The NOESY spectrum of pure PEA+ solution showed a diagonal peak from self-association of each proton, and some cross-peaks that are related to interactions between adjacent protons of -NH3+ (7.94 ppm) toward the -CH2- (2.8\u20133.0\u2009ppm) moiety. In contrast, the spectrum of a PEA-MDA mixture solution showed additional cross-peaks between NH4+ (7.51\u20137.34\u2009ppm) and C6H5 (7.214\u20137.323\u2009ppm); these peaks indicate the presence of cation-\u03c0 interaction with spatially adjacent protons from two ions22<\/a>. The binding energy of cation\u2212\u03c0 interaction between NH4+ and \u03c0 electrons in C6H5 is reported to be significantly high, reaching up to ~18\u2009kcal\u2009mol\u22121, which can be arguably the strongest compared with any of the other noncovalent interactions in precursor solution, including hydrogen bonding, thereby coordinating NH4+ and C6H523<\/a>,24<\/a>. The 2D Diffusion-Ordered Spectroscopy (DOSY) NMR also revealed that the diffusivity of NH4+ ions (\u2009~\u20097.3\u2009ppm) was decreased from 5.25\u2009\u00d7\u200910\u221210\u2009m2\u2009s\u22121 in the MDACl2 solution to 4.85\u2009\u00d7\u200910\u221210\u2009m2\u2009s\u22121 in the PEABr\/MDACl2 mixture, indicating the coordination of NH4+ with \u03c0 electrons in PEA+ from the formation of a strong cation-\u03c0 intermediate complex (Supplementary Fig.\u00a09<\/a>).<\/p>\n Fig. 2: Intermediate-assisted bright blue-emitting quasi-2D perovskites. a, b NOESY 2D 1H NMR of perovskite precursor solution without MDACl2 (a) and with MDACl2 (b). c Schematic figure on the mechanism of cation-\u03c0 intermediate complex formation. d Schematic illustration of crystallization process with (upper panel) and without (bottom panel) MDACl2 in sequence of solution state, film state after spin-coating, IDP process, and thermal annealing process, each from left to right. Inset of the scheme after spin-coating: Picture of thin films with different time after spin-coating. Scale bar, 1\u2009cm. e Steady-state PL spectra of quasi-2D perovskite thin films with different amount of MDACl2 substitution. f Steady-state PL intensity and FWHM of perovskite films different amount of MDACl2 substitution and A-IDP process. g PLQY and FWHM of perovskite films different amount of MDACl2 substitution and with or without A-IDP process.<\/p>\n Combining these results, the coordination process can be visualized (Fig.\u00a02c<\/a>). The strong cation-\u03c0 interaction of NH4+ with benzene effectively prevented the spontaneous crystallization of PEA+ into low-n phases (Fig.\u00a02d<\/a>). As expected, incorporation of MDACl2 into precursor solution delayed the formation of low-n phases and induced slow homogeneous growth after spin coating (Supplementary Fig.\u00a010<\/a>). Pristine film was already crystallized into photoactive quasi-2D phases without annealing process and thus showed blue emission under a UV lamp. In contrast, the MDACl2-incorporated film showed negligible color and absorbance in the visible range; this change indicates an absence of any crystallized phase during this intermediate stage (inset in Fig.\u00a02d<\/a>).<\/p>\n The coordination chemistry between precursors forms metastable intermediate states, and thereby kinetically delay formation of the thermodynamically stable low-n phases (n\u2009\u2264\u20093). The films now have uniform distribution and maintain the perovskite crystals as an intermediate phase until the annealing process starts. Note that even with intermediate phases, the thermodynamic broadening of quasi-2D crystals toward low-n phases can occur without the IDP process, as confirmed in GIWAXS result of pristine perovskite films with different amount of MDACl2 (Supplementary Fig.\u00a011<\/a>).<\/p>\n The MDACl2-included films with the A-IDP process showed distinct emission characteristics compared with pristine films. With a sufficient amount of MDACl2 incorporated up to 20\u2009mol. %, the uniform and narrowly distributed intermediate phase is achieved, which transformed into homogeneous medium-n phases after A-IDP process. The PL spectra gradually blue-shifted from 500\u2009nm toward 482\u2009nm with narrowed emission spectra after A-IDP process (Fig.\u00a02e<\/a>). Importantly, the broad emission spectra with FWHM of >24\u2009nm was observed with pristine films regardless of molar ratio of MDACl2 (Supplementary Fig.\u00a012<\/a>). This indicates that merely facilitating formation of the kinetically stable intermediate complex is not enough to hinder the disproportion during thermal annealing process; a further requirement is that the complex must be pinned by excess solvent and ligand exchange process before thermodynamical broadening can occur to cause phase inhomogeneity and interfacial defects. Also, with the ideal pinning of medium-n phases in a uniform kinetic stage, A-IDP perovskites with 20\u2009mol. % MDACl2 showed the longest PL lifetime, the highest PLQY of 73%, and a narrow emission spectrum with FWHM\u2009=\u200920.6\u2009nm at 489\u2009nm (Fig.\u00a02f, g<\/a>).<\/p>\n Fast charge-funnelling in distribution-controlled phases<\/p>\n Full exploitation of the benefits of the A-IDP-engineered perovskite films requires understanding of the mechanism by which the intermediate-direct-pinned quasi-2D crystals affects the behavior of charge carriers. To investigate this phenomenon, we conducted time-resolved spectroscopic studies of the perovskite films. Charge-carrier funnelling in the perovskite films was directly assessed using femtosecond transient absorption (fs-TA) measurements. By pumping at \u03bb\u2009=\u2009400\u2009nm, we generated a population of charge carriers at the energy state of the 2D perovskite crystals (n\u2009=\u20091). Pump fluence was kept low (1.4\u2009\u00d7\u20091017\u2009cm\u22122) to minimize high-order recombination processes and avoid complicating the carrier-relaxation dynamics.<\/p>\n Immediately after photoexcitation, the initial ground state bleaching (GSB) signal within the 450 \u2264 \u03bb\u2009\u2264\u2009490\u2009nm (n\u2009=\u20093\u20135) indicated that the charge carriers were rapidly funnelled to the lowest states of medium-n phases (Fig.\u00a03a\u2013d<\/a>). In the pristine film, the TA spectral evolution revealed the initial GSB maximum at 450\u2009nm (n\u2009=\u20093) vanishing and evolving into 470\u2009nm (n\u2009=\u20094) within hundreds of femtoseconds (Fig.\u00a03c, e<\/a>). This observation suggests state-to-state energy funnelling towards the emitting states at progressively lower energies. In stark contrast, in the A-IDP film, the GSB signal was initially absent at 450\u2009nm (n\u2009=\u20093) and was mainly distributed near 488\u2009nm (n\u2009=\u20095) (Fig.\u00a03d, f<\/a>); this skipping of the n\u2009=\u20093 state indicates highly-rapid funnelling of charge carriers to the lowest state, within the instrument\u2019s temporal resolution of 170\u2009fs, which may have been triggered by different distribution of density of states (DOS) (Fig.\u00a03g<\/a>). Over hundreds of femtoseconds, the GSB signal increased and its peak gradually redshifted; these indicate the ongoing energy funnelling across the quasi-2D manifold.<\/p>\n Fig. 3: Femtosecond TA spectra of pristine and A-IDP perovskite films. a, b 2D contour plot and c, d early-time spectra of pristine (a, c) and A-IDP (b, d) films. e, f TA kinetic traces of pristine (e) and A-IDP (f) perovskite films probed at 450\u2009nm, 470\u2009nm, 488\u2009nm, each corresponding to domains of n\u2009=\u20093,4,5, respectively. g Schematic description of the charge carrier funnelling occurring in pristine and A-IDP films. The DOS were qualitatively estimated from the initial carrier population distribution (TA spectra at t\u2009=\u20090.2\u2009ps). h Carrier population distribution of pristine and A-IDP films presented by the weighted average peak area of TA spectra at delay times 0.2\u2009ps (upper panels) and 1\u2009ps (lower panels).<\/p>\n The red edge of the GSB developed a derivative-like photoinduced absorption (PA) feature, which was pronounced in the A-IDP film but was negligible in the pristine film (Fig.\u00a03c, d<\/a> and Supplementary Fig.\u00a013a, b<\/a>). One origin of this PA feature may be the relatively reduced sub-bandgap defect states in A-IDP film compared to that in pristine film, as indicated by the lower absorbance of the red tail in UV-Vis spectra (Fig.\u00a01f<\/a>). The weaker GSB signal on the lower energy side of excitonic transitions may have contributed to the more prominent appearance of this PA feature. Another possibility is that the PA feature arises from the attractive exciton-exciton interaction25<\/a>, and the observed stronger exciton-exciton interaction in A-IDP film evidences for a relatively random orientation of the crystals within the film. In quasi-2D perovskites, the organic layers tend to dielectrically confine the exciton within the inorganic crystal along the out-of-plane direction. Excitons that are strongly confined within the crystal are well isolated dielectrically, reducing the likelihood of interaction with the excitons in neighboring crystals, especially when crystals are orderly packed. However, when the crystals are randomly oriented, the dielectric confinement experienced by an exciton is partially canceled out by the differently oriented neighboring crystals. This reduction in dielectric screening increases the likelihood of interaction between excitons in adjacent crystals. These overall improve the spatial accessibility of excitons in neighboring inorganic octahedral layers, greatly facilitating the energy funnelling across the excitonic manifold in A-IDP film and ultimately benefiting the LED device efficiency.<\/p>\n To elucidate the specific pathway and rate of charge carrier funnelling, TA kinetics were analysed at each energy states of \u03bb\u2009=\u2009450\u2009nm, 470\u2009nm, and 488\u2009nm corresponding to the n\u2009=\u20093, 4, and 5, respectively (Fig.\u00a03e, f<\/a>). In the pristine film, the charge carriers initially accumulated at n\u2009=\u20093 and rapidly decayed, following a double-exponential function with decay-time constants of 220\u2009fs and 400\u2009fs (Fig.\u00a03e<\/a>). These decay constants perfectly matched with the rise time constants of the n\u2009=\u20094 and n\u2009=\u20095 state populations, directly verifying the carrier-funnelling pathway from n\u2009=\u20093 to n\u2009=\u20094 (220\u2009fs) and from n\u2009=\u20093 to n\u2009=\u20095 (400\u2009fs). In contrast, the n\u2009=\u20094 population showed negligible decay with a slow time constant of 1,500\u2009fs; this slow rate indicates inefficient carrier funnelling from n\u2009=\u20094 to n\u2009=\u20095 in the pristine quasi-2D perovskite despite their energetic proximity. This inefficiency is attributed to the lower proportion of n\u2009=\u20095 states and the unfavorable (well-ordered, dielectrically screened) orientation of quasi-2D crystals in the film.<\/p>\n In contrast, the A-IDP film demonstrated distinct behavior, with most of the carrier population initially accumulating at n\u2009=\u20095 with a rise-time constant of 264\u2009fs, which was 1.5 times faster compared to the pristine film\u2019s 400-fs funnelling time to n\u2009=\u20095 (Fig.\u00a03e, f<\/a>). Furthermore, charge carriers accumulated at n\u2009=\u20094 showed a 400-fs decay, concurrent with the second rise-constant of the n\u2009=\u20095 signal, effectively depleting the carrier population at n\u2009=\u20094 by efficient energy funnelling. The carrier population was negligible at n\u2009=\u20093; because of this, the n\u2009=\u20093 kinetic trace was overwhelmed by the excited-state absorption (ESA) signal, the dynamics of which merely followed the decay of the n\u2009=\u20094 state. Thus, the charge-carrier funnelling in the A-IDP film differed from that in the pristine film by (i) direct funnelling of carriers mostly to n\u2009=\u20095 with no accumulation at n\u2009=\u20093 (within the temporal resolution) and (ii) effective funnelling away of the remaining carriers at n\u2009=\u20094 (Fig.\u00a03g<\/a>).<\/p>\n To further clarify the energy-funnelling pathway, we analysed the charge-carrier distribution across different n domains over time using the reported quantification method10<\/a>. We fitted the TA spectra (Fig.\u00a03c, d<\/a>) using multiple Gaussian functions to quantify the contribution of each domain\u2019s transition (Supplementary Fig.\u00a014<\/a>). The population distribution was initially obtained at a delay time of 0.2\u2009ps (upper panel of Fig.\u00a03h<\/a>). In the pristine film, charge carriers predominantly accumulated at n\u2009=\u20093, whereas in the A-IDP film, most of the charge carriers were efficiently funnelled to the n\u2009=\u20095 state. At a delay time of 1\u2009ps, when the dynamics of hundreds of femtoseconds had been nearly completed, the carrier population at n\u2009=\u20093 in the pristine film was partly shifted to n\u2009=\u20094 and n\u2009=\u20095, but the population remained smaller at n\u2009=\u20095 than at n\u2009=\u20094 (n\u2009=\u20095 to n\u2009=\u20094 population <1). In contrast, in the A-IDP film, at a time delay of 1\u2009ps, the n\u2009=\u20093 population was fully depleted by funnelling, and the population ratio of n\u2009=\u20095 to n\u2009=\u20094 had increased to nearly 4:1.<\/p>\n Additional fs-TA measurements were conducted to investigate the function of the CCA as an anchor molecule at the crystal surface. TA dynamics of the S-IDP film without the CCA molecule was compared with that of the A-IDP film with the CCA molecule. The difference in TA dynamics between two films was pronounced at higher pump fluence (4.1\u2009\u00d7\u20091017\u2009cm\u22122). The initial TA spectrum of the S-IDP film showed a GSB shoulder at 450\u2009nm, which was absent in the A-IDP film; this evidences a partial accumulation of charge carriers at n\u2009=\u20093 in the S-IDP film (Supplementary Fig.\u00a015a, b<\/a>). Furthermore, introduction of CCA clearly shortened the decay constant of the n\u2009=\u20094 state in A-IDP (370\u2009fs) compared to that in S-IDP (434\u2009fs) (Supplementary Fig.\u00a015c<\/a>) and also the corresponding rise constant of n\u2009=\u20095 state in A-IDP (354\u2009fs) compared to that in S-IDP (456\u2009fs), showing the accelerated carrier funnelling towards n\u2009=\u20095 (Supplementary Fig.\u00a015d<\/a>).<\/p>\n The carrier population distributions of A-IDP and S-IDP films clearly illustrate the energy funnelling pathway, as seen in both films at 0.2\u2009ps, where the initial distribution was similar, besides a smaller n\u2009=\u20093 contribution in A-IDP film than in S-IDP film (Supplementary Figs.\u00a015e<\/a> and 13<\/a>). However, at 1\u2009ps, a larger portion of the n\u2009=\u20094 population had been funnelled into n\u2009=\u20095 in the A-IDP film compared to that in the S-IDP film. Such a difference indicates that the presence of the CCA additive molecule increases the overall energy-funnelling rate by specifically accelerating the n\u2009=\u20094 to n\u2009=\u20095 pathway. CCA substitutes PEA and binds to perovskite layers with a smaller molecule size, thereby reducing the Van der Waals gap between neighboring quasi-2D perovskite crystals. This additive effect was more clearly observed as the pump fluence was increased, which suggests that the effect of CCA was more pronounced in the presence of the phonon-bottleneck effect. Smaller Van der Waals gap between the quasi-2D crystals reduces the density of states for phonons, and thereby facilitates the charge-carrier funnelling even at high initial carrier density26<\/a>,27<\/a>.<\/p>\n Therefore, we suggest that the rearrangement of crystals upon IDP treatment, whether with or without the additive, smooths the energetic landscape of the film and facilitates carrier funnelling into domains with higher n by preventing charge accumulation in lower n domains. Further, the inclusion of CCA molecules chemically optimized the crystal orientations within the film to further facilitate interdomain charge transfer, which was found to be particularly effective between the medium-n phases (n\u2009=\u20094, 5). Thus, the efficient energy funnelling in optimized IDP quasi-2D perovskite films in this study is attributed to the interplay between the engineered energy landscape, the reorientation of quasi-2D crystals, and the finely-tuned Van der Waals gap between adjacent quasi-2D crystals.<\/p>\n Efficient and narrow sky-blue emission<\/p>\n To exploit the dominant phase distribution of medium-n phases and the fast charge-transport characteristics, we developed sky-blue emitting PeLEDs that use A-IDP quasi-2D perovskites (Fig.\u00a04a<\/a>). The development of sky-blue LEDs represents an important step toward achieving efficient deep-blue emission. This approach mirrors the strategy used in the development of stable blue organic light-emitting diodes (OLEDs) with a microcavity structure, where sky-blue OLEDs were preferred due to their much longer lifetimes28<\/a>,29<\/a>. Similarly, given the short lifetimes typically observed in deep-blue PeLEDs, sky-blue PeLEDs\u2014offering longer lifetimes and higher efficiency\u2014could be advantageous until stable and efficient deep-blue PeLEDs are realized. These devices, when combined with a microcavity effect that shifts the sky-blue spectra towards deeper blue, present a promising approach. From this perspective, developing an ideal material system for sky-blue emission is critical, as it can enable efficient and stable deep-blue emission following optical cavity engineering. Moreover, stable and narrow sky-blue light sources are valuable for their role in creating efficient and stable white LEDs when combined with yellow phosphors. Specifically, narrow backlight emission provides two key advantages: (1) higher power efficiency and (2) better spectral stability of white emission by avoiding unintended backlight leakage in wavelength ranges that the phosphor cannot absorb30<\/a>.<\/p>\n Fig. 4: EL characteristics of blue PeLEDs. a schematic energy diagram of PeLEDs. b luminance and current density vs voltage, c EQE vs current density (inset: operating PeLEDs without (left) and with (right) hemispherical lens, scale bar: 1\u2009cm), d normalized EL spectra, e EQE histogram of PeLEDs. f Characteristics of reported blue PeLEDs with peak emission wavelength <495\u2009nm based on maximum EQE and EL linewidth. Summarized in Supplementary Table\u00a03<\/a>. g Photograph of operating large-area PeLEDs (pixel size: 900 mm2). Scale bar: 1\u2009cm. h Schematic structure and picture of operating 30\u2009\u00d7\u200910 passive-matrix PeLEDs (active area\u2009=\u2009200\u2009\u03bcm\u2009\u00d7 600\u2009\u03bcm). Scale bar: 1\u2009mm.<\/p>\n Transient EL measurement of PeLEDs showed faster rising time at the onset of the voltage pulse and EL decay time after the voltage pulse off in A-IDP PeLEDs than in S-IDP and pristine PeLEDs, as a result of accelerated carrier transfer in A-IDP PeLEDs (Supplementary Fig.\u00a016a\u2013c<\/a>). The A-IDP perovskites films also exhibited an order higher lateral conductivity (\u03c3) compared to that of pristine perovskite film (Supplementary Fig.\u00a017<\/a>). Benefiting from the high PLQY and accelerated charge transport, the A-IDP PeLEDs showed maximum EQE of 22.5% (current efficiency\u2009=\u200926.62\u2009cd\u2009A\u22121) at \u03bb\u2009=\u2009489\u2009nm (FWHM\u2009=\u200920.8\u2009nm), calculated using the full angular EL distribution (Fig.\u00a04b\u2013d<\/a>, Supplementary Fig.\u00a018<\/a> and Supplementary Table\u00a01<\/a>). The summarized EL characteristics of pristine and A-IDP PeLEDs with different amounts of MDACl2 and CCA agree well with the tendency in PL characteristics (Supplementary Figs.\u00a019<\/a>, 20<\/a> and Supplementary Table\u00a02<\/a>). We further increased the EQE of our PeLEDs to 41.8% by placing a light-outcoupling hemispherical lens on the emitting glass substrate. Compared to pristine PeLEDs, which exhibit a turn-on voltage greater than 3.0\u2009V, both S-IDP and A-IDP PeLEDs showed a sub-gap turn-on voltage of 2.2\u2009V\u2014below the bandgap (Eg\u2009=\u20092.54\u2009eV). This observation can be attributed to the recombination of non-thermal-equilibrium band-edge carriers in the emitting layer, where the carrier populations are perturbed by a small external bias, leading to radiative recombination below the turn-on voltage31<\/a>,32<\/a>. Furthermore, PeLEDs processed via the IDP method benefited from improved charge transport and recombination of band-edge carriers, which can be attributed to the suppression of charge accumulation in low-n phases. Also, the EQE histogram of A-IDP PeLEDs (average\u2009=\u200919.7\u2009\u00b1\u20091.2%, 37 devices) shows that our strategy can provide highly reproducible quasi-2D perovskite thin films for blue emission (Fig.\u00a04e<\/a>).<\/p>\n These PeLEDs are an advance in that previously-reported high-efficiency PeLEDs have been largely limited to green emission by using single-halide composites. Previous PeLEDs that used mixed-halide composite, which is important to induce a blue shift, showed significantly decreased emission efficiency at \u03bb\u2009<\u2009500\u2009nm due to halide segregation and the resulting inhomogeneity in the energy landscape. In contrast, by homogeneously anchoring medium-n quasi-2D phases, we achieved a remarkably high EQE of 22.5% in the sky-blue emission region (Supplementary Table\u00a03<\/a>). Moreover, remarkably narrow EL linewidth (108\u2009meV) of our PeLEDs among efficient quasi-2D blue PeLEDs (EQE\u2009>\u200915%) evidences the advantage of ideal energy landscape in quasi-2D emitter structure achieved by the A-IDP method (Fig.\u00a04f<\/a>). The A-IDP PeLEDs also showed stable EL operation without significant spectral shift (\u0394\u03bb\u2009~\u20091\u2009nm at 1000\u2009cd\u2009m\u22122), compared with that of pristine PeLEDs (\u0394\u03bb\u2009~\u20092\u2009nm at <100\u2009cd\u2009m\u22122) (Supplementary Fig.\u00a016d<\/a>). We also fabricated PeLEDs with emission spectra from deep-blue (469\u2009nm) to green (504\u2009nm) region based on A-IDP process; these have EQEs of 5.7% for 469\u2009nm and 12.5% for 479\u2009nm, and 21.7% for 504\u2009nm, respectively (Supplementary Fig.\u00a021<\/a>).<\/p>\n Device stability of the PeLEDs were compared by monitoring the luminance under constant current operation. Compared with the pristine PeLEDs having half-lifetimes of T50\u2009=\u20091\u2009min at initial brightness L0\u2009=\u200950\u2009cd\u2009m\u22122, A-IDP PeLEDs showed 150 times longer T50\u2009=\u20092.5\u2009h at L0\u2009=\u2009100\u2009cd\u2009m\u22122, realizing remarkably long operational half-lifetime among PeLEDs with \u03bb\u2009<\u2009500\u2009nm (Supplementary Fig.\u00a016e, f<\/a>). Benefiting from the enhanced stability and ultralow turn-on voltage, we fabricated large-area blue PeLEDs (pixel size: 900\u2009mm2) successfully with high uniformity (Fig.\u00a04g<\/a>). Also, we developed the first blue-emitting passive-matrix PeLEDs with 30\u2009\u00d7\u200910 arrays (active area\u2009=\u2009200\u2009\u03bcm\u2009\u00d7\u2009600\u2009\u03bcm) by photolithographic ITO electrode patterning, providing uniform blue emission among adjacent pixels. (Fig.\u00a04h<\/a>). These highlights the potential applications of PeLEDs to addressable full-color panel displays.<\/p>\n We demonstrated an anchoring-assisted intermediate direct pinning (A-IDP) process to achieve efficient and narrow-emitting quasi-2D perovskite structure. The A-IDP process enabled formation of medium-n phases (n\u2009=\u20094\u22125) by removing excess large cation and by kinetically pinning the uniformly-distributed intermediate phases. The A-IDP process uses a CCA molecule, which became incorporated as a molecular anchor at the surface of quasi-2D crystals, and maximized the charge transport between crystals. The perovskites produced using A-IDP showed improved luminescent efficiency and fast charge funnelling toward medium-n phases. As a result, we developed efficient blue PeLEDs at 489\u2009nm with maximum EQE\u2009=\u200922.5%, the narrow EL linewidth of 108\u2009meV among quasi-2D blue PeLEDs, and greatly improved device operational lifetime. We extended our approach to the first demonstration of blue-emitting passive matrix LEDs (30\u2009\u00d7\u200910 arrays, active area\u2009=\u2009200\u2009\u03bcm\u2009\u00d7\u2009600\u2009\u03bcm) with great pixel clarity. Our blue PeLEDs demonstrate the great potential of high-efficiency perovskite emitters for narrow blue emission and provide valuable insights to guide further development of blue emission, which can be exploited to realize full-color displays.<\/p>\n","protected":false},"excerpt":{"rendered":"Anchoring-assisted intermediate direct pinning process The broad phase distribution of quasi-2D perovskites is mainly attributed to the rapid…\n","protected":false},"author":2,"featured_media":115816,"comment_status":"","ping_status":"","sticky":false,"template":"","format":"standard","meta":{"footnotes":""},"categories":[24],"tags":[22800,2026,61,60,19952,69785,2027,248,82],"class_list":{"0":"post-115815","1":"post","2":"type-post","3":"status-publish","4":"format-standard","5":"has-post-thumbnail","7":"category-physics","8":"tag-electronic-devices","9":"tag-humanities-and-social-sciences","10":"tag-ie","11":"tag-ireland","12":"tag-lasers","13":"tag-leds-and-light-sources","14":"tag-multidisciplinary","15":"tag-physics","16":"tag-science"},"_links":{"self":[{"href":"https:\/\/www.newsbeep.com\/ie\/wp-json\/wp\/v2\/posts\/115815","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/www.newsbeep.com\/ie\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/www.newsbeep.com\/ie\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/www.newsbeep.com\/ie\/wp-json\/wp\/v2\/users\/2"}],"replies":[{"embeddable":true,"href":"https:\/\/www.newsbeep.com\/ie\/wp-json\/wp\/v2\/comments?post=115815"}],"version-history":[{"count":0,"href":"https:\/\/www.newsbeep.com\/ie\/wp-json\/wp\/v2\/posts\/115815\/revisions"}],"wp:featuredmedia":[{"embeddable":true,"href":"https:\/\/www.newsbeep.com\/ie\/wp-json\/wp\/v2\/media\/115816"}],"wp:attachment":[{"href":"https:\/\/www.newsbeep.com\/ie\/wp-json\/wp\/v2\/media?parent=115815"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/www.newsbeep.com\/ie\/wp-json\/wp\/v2\/categories?post=115815"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/www.newsbeep.com\/ie\/wp-json\/wp\/v2\/tags?post=115815"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}![\"figure](\"https:\/\/www.newsbeep.com\/ie\/wp-content\/uploads\/2025\/11\/41467_2025_62863_Fig1_HTML.png\")
<\/a><\/p>\n![\"figure](\"https:\/\/www.newsbeep.com\/ie\/wp-content\/uploads\/2025\/11\/41467_2025_62863_Fig2_HTML.png\")
<\/a><\/p>\n![\"figure](\"https:\/\/www.newsbeep.com\/ie\/wp-content\/uploads\/2025\/11\/41467_2025_62863_Fig3_HTML.png\")
<\/a><\/p>\n![\"figure](\"https:\/\/www.newsbeep.com\/ie\/wp-content\/uploads\/2025\/11\/41467_2025_62863_Fig4_HTML.png\")
<\/a><\/p>\n